The objective of this book was investigated to evaluate mechanical and machinability characteristics of Glass-fiber-Reinforced Aluminium (Glare) laminates as well as Aluminium sheets of same thickness. In addition to that the tensile and flexural strength of Glare laminates were compared with values of aluminium sheets. In this project, the aluminium based FMLs were fabricated using hand layup technique and cut as per ASTM standards. Three types of layers such as 2/1 Glare, 3/2 Glare and 5/4 Glare laminates were prepared. Computer controlled UTM machine used to determine the tensile, flexural...

L'objectif de ce livre est d'évaluer les caractéristiques mécaniques et d'usinabilité des stratifiés d'aluminium renforcé de fibres de verre (Glare) ainsi que des feuilles d'aluminium de même épaisseur. En outre, la résistance à la traction et à la flexion des stratifiés Glare a été comparée aux valeurs des feuilles d'aluminium. Dans ce projet, les FML à base d'aluminium ont été fabriqués à l'aide d'une technique de stratification manuelle et découpés conformément aux normes ASTM. Trois types de couches ont été préparés : 2/1 Glare, 3/2 Glare et 5/4 Glare. Une...

Das Ziel dieses Buches bestand darin, die mechanischen und maschinellen Eigenschaften von glasfaserverstärkten Aluminiumlaminaten (Glare) sowie von Aluminiumblechen gleicher Dicke zu untersuchen. Darüber hinaus wurde die Zug- und Biegefestigkeit von Glare-Laminaten mit den Werten von Aluminiumblechen verglichen. In diesem Projekt wurden die aluminiumbasierten FMLs im Handauflegeverfahren hergestellt und gemäß den ASTM-Standards geschnitten. Es wurden drei Arten von Schichten hergestellt, nämlich 2/1 Glare-, 3/2 Glare- und 5/4 Glare-Laminate. Mit einer computergesteuerten UTM-Maschine...