Tin Nano Catalyst for Bayer-Villiger Oxidation Reaction » książka
Tin Nano Catalyst for Bayer-Villiger Oxidation Reaction
ISBN-13: 9783659331206 / Angielski / Miękka / 2015 / 88 str.
Highly ordered mesoporous SBA-15 silica material was synthesized under hydrothermal conditions using P123 as template and tetraethyl orthosilicate as silica source. Tin nanoparticles were deposited on the pore surfaces of Si-SBA-15 support post synthetically using SnCl4 as tin source. Tin containing SBA-15 catalysts were also prepared by direct synthesis using SnCl4 and SBA-15 precursors under hydrothermal conditions. These Sn-SBA-15 catalysts were further modified by adding trifluromethane sulfonic acid (F3CH-SO3H). These Sn-SBA-15-OTf catalysts were characterized by low angle XRD and N2 adsorption-desorption techniques to investigate the structural intactness of SBA-15 after every modification. The deposition of Sn, its crystalline behavior, particle size, local environments and morphological aspects were characterized by FT-IR, XRD, UV-vis, XPS and SEM techniques respectively. The loading amount of Tf-OH was confirmed by CHNS analysis. Sn-SBA-15-OTf catalyst was found to be highly active and selective towards the Baeyer-Villiger oxidation of cyclohexane to -caprolactone in the liquid phase as heterogeneous catalyst."
Highly ordered mesoporous SBA-15 silica material was synthesized under hydrothermal conditions using P123 as template and tetraethyl orthosilicate as silica source. Tin nanoparticles were deposited on the pore surfaces of Si-SBA-15 support post synthetically using SnCl4 as tin source. Tin containing SBA-15 catalysts were also prepared by direct synthesis using SnCl4 and SBA-15 precursors under hydrothermal conditions. These Sn-SBA-15 catalysts were further modified by adding trifluromethane sulfonic acid (F3CH-SO3H). These Sn-SBA-15-OTf catalysts were characterized by low angle XRD and N2 adsorption-desorption techniques to investigate the structural intactness of SBA-15 after every modification. The deposition of Sn, its crystalline behavior, particle size, local environments and morphological aspects were characterized by FT-IR, XRD, UV-vis, XPS and SEM techniques respectively. The loading amount of Tf-OH was confirmed by CHNS analysis. Sn-SBA-15-OTf catalyst was found to be highly active and selective towards the Baeyer-Villiger oxidation of cyclohexane to ε-caprolactone in the liquid phase as heterogeneous catalyst.
Czytaj nas na:
KrainaKsiazek.PL - Księgarnia Internetowa