CNWs loaded poly(SA)hydrogel Its Swelling and mechanical properties » książka
CNWs loaded poly(SA)hydrogel Its Swelling and mechanical properties
ISBN-13: 9783659557941 / Angielski / Miękka / 2014 / 76 str.
CNWs loaded poly(SA)hydrogel Its Swelling and mechanical properties
ISBN-13: 9783659557941 / Angielski / Miękka / 2014 / 76 str.
(netto: 153,29 VAT: 5%)
Najniższa cena z 30 dni: 160,95 zł
ok. 10-14 dni roboczych
Bez gwarancji dostawy przed świętami
Darmowa dostawa!
In this work, poly (sodium acrylate) hydrogel films, doped with cellulose nano-whiskers (CNWs), are prepared via free radical polymerization of sodium acrylate (SA) in aqueous medium. The CNWs were added into the polymerization feed mixture, in the concentration range of 4.8 to 24.3 wt% of monomer and the resulting CNWs/poly(SA) hydrogel films were investigated for their water absorbency in the physiological fluid (PF) . The addition of CNWs caused a decrease in the equilibrium water uptake. The kinetic water uptake data of all hydrogel samples were best interpreted by the Second order kinetic. The water vapor permeation studies were also carried out. The WVTR of all the film samples were quite low. The mechanical properties of films such as Tensile Strength (TS) and Percent Elongation (PE) varied with the CNWs content. All the film samples showed fair folding endurance (FE), with more than 600 times folding without suffering from any crack.
In this work, poly (sodium acrylate) hydrogel films, doped with cellulose nano-whiskers (CNWs), are prepared via free radical polymerization of sodium acrylate (SA) in aqueous medium. The CNWs were added into the polymerization feed mixture, in the concentration range of 4.8 to 24.3 wt% of monomer and the resulting CNWs/poly(SA) hydrogel films were investigated for their water absorbency in the physiological fluid (PF) . The addition of CNWs caused a decrease in the equilibrium water uptake. The kinetic water uptake data of all hydrogel samples were best interpreted by the Second order kinetic. The water vapor permeation studies were also carried out. The WVTR of all the film samples were quite low. The mechanical properties of films such as Tensile Strength (TS) and Percent Elongation (PE) varied with the CNWs content. All the film samples showed fair folding endurance (FE), with more than 600 times folding without suffering from any crack.