Welding Metallurgy and Weldability

ISBN-13: 9781118230701 / Angielski / Twarda / 2014 / 432 str.

John C. Lippold

Opis

Describes the weldability aspects of structural materials used in a wide variety of engineering structures, including steels, stainless steels, Ni-base alloys, and Al-base alloys Welding Metallurgy and Weldability describes weld failure mechanisms associated with either fabrication or service, and failure mechanisms related to microstructure of the weldment. Weldability issues are divided into fabrication and service related failures; early chapters address hot cracking, warm (solid-state) cracking, and cold cracking that occur during initial fabrication, or repair. Guidance on failure analysis is also provided, along with examples of SEM fractography that will aid in determining failure mechanisms. Welding Metallurgy and Weldability examines a number of weldability testing techniques that can be used to quantify susceptibility to various forms of weld cracking.

• Describes the mechanisms of weldability along with methods to improve weldability
• Includes an introduction to weldability testing and techniques, including strain-to-fracture and Varestraint tests
• Chapters are illustrated with practical examples based on 30 plus years of experience in the field

Illustrating the weldability aspects of structural materials used in a wide variety of engineering structures, Welding Metallurgy and Weldability provides engineers and students with the information needed to understand the basic concepts of welding metallurgy and to interpret the failures in welded components.

Spis treści

Preface xiii

Author Biography xvi

1 Introduction 1

1.1 Fabrication–Related Defects 5

1.2 Service–Related Defects 6

1.3 Defect Prevention and Control 7

References 8

2 Welding Metallurgy Principles 9

2.1 Introduction 9

2.2 Regions of a Fusion Weld 10

2.3 Fusion Zone 13

2.3.1 Solidification of Metals 15

2.3.2 Macroscopic Aspects of Weld Solidification 24

2.3.4 Solute Redistribution 34

2.3.5 Examples of Fusion Zone Microstructures 40

2.3.6 Transition Zone (TZ) 43

2.4 Unmixed Zone (UMZ) 45

2.5 Partially Melted Zone (PMZ) 48

2.5.1 Penetration Mechanism 50

2.5.2 Segregation Mechanism 53

2.5.3 Examples of PMZ formation 58

2.6 Heat Affected Zone (HAZ) 60

2.6.1 Recrystallization and Grain Growth 61

2.6.2 Allotropic Phase Transformations 63

2.6.3 Precipitation Reactions 66

2.6.4 Examples of HAZ Microstructure 69

2.7 Solid–State Welding 70

2.7.1 Friction Stir Welding 72

2.7.2 Diffusion Welding 76

2.7.3 Explosion Welding 77

2.7.4 Ultrasonic Welding 79

References 81

3 Hot Cracking 84

3.1 Introduction 84

3.2 Weld Solidification Cracking 85

3.2.1 Theories of Weld Solidification Cracking 85

3.2.2 Predictions of Elemental Effects 94

3.2.3 The BTR and Solidification Cracking Temperature Range 97

3.2.4 Factors that Influence Weld Solidification Cracking 102

3.2.5 Identifying Weld Solidification Cracking 112

3.2.6 Preventing Weld Solidification Cracking 116

3.3 Liquation Cracking 119

3.3.1 HAZ Liquation Cracking 119

3.3.2 weld metal Liquation Cracking 122

3.3.3 Variables that Influence Susceptibility to Liquation Cracking 123

3.3.4 Identifying HAZ and weld metal Liquation Cracks 126

3.3.5 Preventing Liquation Cracking 127

References 128

4 Solid–State Cracking 130

4.1 Introduction 130

4.2 Ductility–dip Cracking 130

4.2.1 Proposed Mechanisms 133

4.2.2 Summary of Factors That Influence DDC 139

4.2.3 Quantifying Ductility–Dip Cracking 143

4.2.4 Identifying Ductility–Dip Cracks 145

4.2.5 Preventing DDC 147

4.3 Reheat Cracking 149

4.3.1 Reheat Cracking in Low–Alloy Steels 150

4.3.2 Reheat Cracking in Stainless Steels 155

4.3.3 Underclad Cracking 158

4.3.4 Relaxation Cracking 160

4.3.5 Identifying Reheat Cracking 161

4.3.6 Quantifying Reheat Cracking Susceptibility 163

4.3.7 Preventing Reheat Cracking 166

4.4 Strain–age Cracking 168

4.4.1 Mechanism for Strain–age Cracking 171

4.4.2 Factors That Influence SAC Susceptibility 178

4.4.3 Quantifying Susceptibility to Strain–age Cracking 182

4.4.4 Identifying Strain–age Cracking 189

4.4.5 Preventing Strain–age Cracking 189

4.5 Lamellar Cracking 190

4.5.1 Mechanism of Lamellar Cracking 191

4.5.2 Quantifying Lamellar Cracking 195

4.5.3 Identifying Lamellar Cracking 197

4.5.4 Preventing Lamellar Cracking 198

4.6 Copper Contamination Cracking 201

4.6.1 Mechanism for Copper Contamination Cracking 201

4.6.2 Quantifying Copper Contamination Cracking 203

4.6.3 Identifying Copper Contamination Cracking 205

4.6.4 Preventing Copper Contamination Cracking 205

References 207

5 Hydrogen–Induced Cracking 213

5.1 Introduction 213

5.2 Hydrogen Embrittlement Theories 214

5.2.1 Planar Pressure Theory 216

5.2.2 Surface Adsorption Theory 217

5.2.3 Decohesion Theory 217

5.2.4 Hydrogen–Enhanced Localized Plasticity Theory 218

5.2.5 Beachem s Stress Intensity Model 219

5.3 Factors That Influence HIC 221

5.3.1 Hydrogen in Welds 221

5.3.2 Effect of Microstructure 224

5.3.3 Restraint 228

5.3.4 Temperature 230

5.4 Quantifying Susceptibility to HIC 230

5.4.1 Jominy End Quench Method 231

5.4.2 Controlled Thermal Severity Test 234

5.4.3 The Y–Groove (Tekken) Test 235

5.4.4 Gapped Bead–on–Plate Test 236

5.4.5 The Implant Test 237

5.4.6 Tensile Restraint Cracking Test 243

5.4.7 Augmented Strain Cracking Test 244

5.5 Identifying HIC 245

5.6 Preventing HIC 247

5.6.1 CE Method 251

5.6.2 AWS Method 254

References 259

6 Corrosion 263

6.1 Introduction 263

6.2 Forms of Corrosion 264

6.2.1 General Corrosion 264

6.2.2 Galvanic Corrosion 265

6.2.3 Crevice Corrosion 267

6.2.4 Selective Leaching 268

6.2.5 Erosion Corrosion 268

6.2.6 Pitting 268

6.2.7 Intergranular Corrosion 271

6.2.8 Stress Corrosion Cracking 277

6.2.9 Microbiologically Induced Corrosion 280

6.3 Corrosion Testing 282

6.3.1 Atmospheric Corrosion Tests 282

6.3.2 Immersion Tests 282

6.3.3 Electrochemical Tests 284

References 286

7 Fracture and Fatigue 288

7.1 Introduction 288

7.2 Fracture 290

7.3 Quantifying Fracture Toughness 293

7.4 Fatigue 297

7.5 Quantifying Fatigue Behavior 305

7.6 Identifying Fatigue Cracking 306

7.6.1 Beach Marks 307

7.6.2 River Lines 307

7.6.3 Fatigue Striations 307

7.7 Avoiding Fatigue Failures 309

References 310

8 Failure Analysis 311

8.1 Introduction 311

8.2 Fractography 312

8.2.1 History of Fractography 312

8.2.2 The SEM 313

8.2.3 Fracture Modes 315

8.2.4 Fractography of Weld Failures 320

8.3 An Engineer s Guide to Failure Analysis 333

8.3.1 Site Visit 334

8.3.2 Collect Background Information 335

8.3.3 Sample Removal and Testing Protocol 336

8.3.4 Sample Removal Cleaning and Storage 336

8.3.5 Chemical Analysis 336

8.3.6 Macroscopic Analysis 337

8.3.7 Selection of Samples for Microscopic Analysis 338

8.3.8 Selection of Analytical Techniques 338

8.3.9 Mechanical Testing 339

8.3.10 Simulative Testing 339

8.3.11 Nondestructive Evaluation Techniques 340

8.3.12 Structural Integrity Assessment 340

8.3.13 Consultation with Experts 340

8.3.14 Final Reporting 340

8.3.15 Expert Testimony in Support of Litigation 341

References 342

9 Weldability Testing 343

9.1 Introduction 343

9.2 Types of Weldability Test Techniques 344

9.3 The Varestraint Test 345

9.3.1 Technique for Quantifying Weld Solidification Cracking 346

9.3.2 Technique for Quantifying HAZ Liquation Cracking 350

9.4 The Cast Pin Tear Test 354

9.5 The Hot Ductility Test 357

9.6 The Strain–to–Fracture Test 362

9.7 Reheat Cracking Test 363

9.8 Implant Test for HAZ Hydrogen–Induced Cracking 366

9.9 Gapped Bead–on–Plate Test for Weld Metal HIC 367

9.10 Other Weldability Tests 370

References 371

Appendix A 372

Appendix B 374

Appendix C 383

Appendix D 388

Index 396

O autorze

John C. Lippold received his BS, MS, and PhD degrees in Materials Engineering from Rensselaer Polytechnic Institute. Upon completion of his formal education, Dr. Lippold worked for seven years at Sandia National Laboratories, Livermore, CA, as a member of the technical staff, specializing in stainless steel and high alloy weldability. From 1985 to 1995, Dr. Lippold worked for Edison Welding Institute. From 1995 to the present, he has been on the faculty of the Welding Engineering program at The Ohio State University and was recently named a College of Engineering Distinguished Faculty member.

Blurb

Describes the weldability aspects of structural materials used in a wide variety of engineering structures, including steels, stainless steels, Ni–base alloys, and Al–base alloys

Welding Metallurgy and Weldability describes weld failure mechanisms associated with either fabrication or service, and failure mechanisms related to microstructure of the weldment. Weldability issues are divided into fabrication and service related failures; early chapters address hot cracking, warm (solid–state) cracking, and cold cracking that occur during initial fabrication, or repair. Guidance on failure analysis is also provided, along with examples of SEM fractography that will aid in determining failure mechanisms. Welding Metallurgy and Weldability examines a number of weldability testing techniques that can be used to quantify susceptibility to various forms of weld cracking. 

• Describes the mechanisms of weldability along with methods to improve weldability
• Includes an introduction to weldability testing and techniques, including strain–to–fracture and Varestraint tests
• Chapters are illustrated with practical examples based on 30 plus years of experience in the field

Illustrating the weldability aspects of structural materials used in a wide variety of engineering structures, Welding Metallurgy and Weldability provides engineers and students with the information needed to understand the basic concepts of welding metallurgy and to interpret the failures in welded components. 

John C. Lippold received his BS, MS, and PhD degrees in Materials Engineering from the Rensselaer Polytechnic Institute. Upon completion of his formal education, Dr. Lippold worked for seven years at Sandia National Laboratories as a member of the technical staff, specializing in stainless steel and high alloy weldability. From 1985 to 1995, Dr. Lippold worked for Edison Welding Institute. From 1995 to the present, he has been on the faculty of the Welding Engineering program at The Ohio State University and was recently named a College of Engineering Distinguished Faculty member.