Synthesis of In2S3 by Spray Pyrolysis : Substrate Temperature Effect on Properties of Sprayed In2S3 Films

ISBN-13: 9786202009270 / Angielski / Miękka / 2017 / 52 str.

Noureddine Bouguila; Ibrahim Halidou; Mabrouk Kraini

Opis

The aim of this research is to investigate the influence of substrate temperature on structural, morphological, optical and electrical properties of In2S3 films. These films have been grown on glass substrates by spray pyrolysis technique. The deposition was carried out at 300-500°C substrate temperature and the molar ratio S/In was fixed to 2. X-ray diffraction analysis shows that the films are polycrystalline and the obtained material is In2S3 with a cubic phase oriented preferentially towards (400). The film grain size increases from 25 to 31 nm whereas the microstrain decreases from 4.69 10-3 to 3.86 10-3 with increasing substrate temperature. The average surface roughness passes through a minimum at substrate temperature of 340°C. Optical transmission of 80% has been achieved in the visible and near infrared regions. The band gap energy has been found in the range of 2.33-2.65 eV. Optical constants were determined by the Wemple-Didomenico model. Hall Effect measurements were carried out for higher substrate temperatures ( 460°C).

O autorze

N. Bouguila completed his PhD in 2000 from the Faculty of Sciences of Tunis, Tunisia. He is currently an assistant professor in the Faculty of Sciences in Gabes University. M. Kraini received a Phd Degree in Physics in 2016 from the University of Monastir. I. Halidou currently teaches at Abdou-Moumouni University of Niamey, Niger.