Novel Thermoplastic Elastomeric Blends of Polystyrene » książka
Novel Thermoplastic Elastomeric Blends of Polystyrene
ISBN-13: 9783659596773 / Angielski / Miękka / 2015 / 128 str.
Thermoplastic elastomeric blends of Polystyrene (PS) and Exudated Resin (ER) are prepared by solution casting technique. The nature of solvent diffusion through the prepared blends of Exudated Resin and Polystyrene of different compositions are studied at various temperatures. Swelling experiment has been conducted in benzene as the solvent to investigate the solvent resistance properties of these blends. The important parameters such as diffusion, sorption and permeation coefficients are calculated and the effect of blend ratio on these parameters is also studied. The activation energies of diffusion are estimated from the sorption data. An anomalous behavior is observed for most of the blend compositions. Thermogravimetric analysis was employed to determine the decomposition behavior of these blends. The dependence of blend composition and cross-linking on the thermal behavior of ER/PS blend system was studied. It is observed that the addition of exudated resin into polystyrene improves the thermal stability. X-ray diffraction technique was employed to study the crystalline nature of the blend system.Resin can be effectively used to reduce the brittleness of polystyrene.
Thermoplastic elastomeric blends of Polystyrene (PS) and Exudated Resin (ER) are prepared by solution casting technique. The nature of solvent diffusion through the prepared blends of Exudated Resin and Polystyrene of different compositions are studied at various temperatures. Swelling experiment has been conducted in benzene as the solvent to investigate the solvent resistance properties of these blends. The important parameters such as diffusion, sorption and permeation coefficients are calculated and the effect of blend ratio on these parameters is also studied. The activation energies of diffusion are estimated from the sorption data. An anomalous behavior is observed for most of the blend compositions. Thermogravimetric analysis was employed to determine the decomposition behavior of these blends. The dependence of blend composition and cross-linking on the thermal behavior of ER/PS blend system was studied. It is observed that the addition of exudated resin into polystyrene improves the thermal stability. X-ray diffraction technique was employed to study the crystalline nature of the blend system.Resin can be effectively used to reduce the brittleness of polystyrene.
Czytaj nas na:
KrainaKsiazek.PL - Księgarnia Internetowa