Fracture Resistance of Titanium and Zirconia Abutments - A Lab Study

ISBN-13: 9783659617287 / Angielski / Miękka / 2014 / 120 str.

Foong Jamie

Opis

Statement of Problem. There is little conclusive evidence comparing the fracture resistance of internal connection titanium and zirconia implant abutments and the purpose of this study was to determine the fracture resistance of internal connection titanium and zirconia implant abutments. Material and Methods. Twenty-two specimens simulating implant-supported anterior single crowns were randomly divided into two equal test groups. Abutments were attached to dental implants mounted in acrylic resin and CAD/CAM crowns constructed. Chewing function was simulated using cyclic loading in a stepped fatigue loading protocol until failure. Failed specimens were then analyzed using SEM and fractographic analysis. Results. The titanium abutment group fractured at a mean ± SD load of 270 ± 56.7 N and a mean ± SD of 81,935 ± 27,929 cycles. The zirconia abutment group fractured at a mean ± SD load of 140 ± 24.6 N and a mean ± SD of 26,296 ± 9,200 cycles (p < 0.005). Conclusions. Within the limitations of this laboratory study, one-piece zirconia abutments exhibit a significantly lower fracture resistance than titanium abutments when using this test protocol (p < 0.0005).

O autorze

Dr. Jamie Foong is a specialist Prosthodontist from Brisbane, Australia. He completed his undergraduate dental degree and specialist degree in Prosthodontics at the University of Melbourne. Jamie has worked in specialist private practice in Melbourne CBD and returned to Brisbane to establish his own private practice.